Sethibela-mollo se se nang halogen joalo ka APP, AHP, MCA se fana ka melemo e meholo ha se sebelisoa polasetiking. Se sebetsa e le sethibela-mollo se sebetsang hantle, se eketsa ho hanyetsa mollo ha thepa. Ho feta moo, se thusa ho ntlafatsa thepa ea polasetiki ea mechini le mocheso, e leng se etsang hore e tšoarelle haholoanyane le ho hanela mocheso o phahameng.
polasetiki e thibelang malakabe PP
Tlhaloso ea Sehlahisoa: TF-241 e na le P le N haholo-holo, ke mofuta oa sethibela-malakabe se se nang halogen tikolohong bakeng sa polyolefin. E ntlafalitsoe haholo-holo bakeng saPP tse fapanengTF-241 e nang le mohlodi wa asiti, mohlodi wa kgase le mohlodi wa khabone, e qala ho sebetsa ka ho thehwa ha char le mokgwa wa ho kenella ha disele.
Molemo:PP e thibelang malakabe e phekotsoeng ke TF-241 e na le khanyetso e betere ea metsi. E ntse e na le ts'ebetso e ntle ea ho thibela malakabe (UL94-V0) kamora ho belisa lihora tse 72 metsing a 70℃.
PP(3.0-3.2mm) e nang le 22% TF-241 e ka pasa liteko tsa UL94 V-0 le GWIT 750℃ / GWFI 960℃.
PP (1.5-1.6mm) e nang le bophahamo ba TF-241 ba 30% e ka feta liteko tsa UL94 V-0.
Leqephe la Lintlha tsa Tekheniki / Tlhaloso:
| Tlhaloso | TF-241 |
| Ponahalo | Phofo e tšoeu |
| P2O5dikahare (ka hare/ka hare) | ≥52% |
| Dikahare tsa N (w/w) | ≥18% |
| Mongobo (w/w) | ≤0.5% |
| Bongata ba bongata | 0.7-0.9 g/cm3 |
| Mocheso oa ho Bola | ≥260℃ |
| Boholo bo tloaelehileng ba likaroloana (D50) | hoo e ka bang 18µm |
Litšobotsi:
1. Phofo e tšoeu, e hanyetsa metsi hantle.
2. Ho hlahisa mosi o fokolang ka bongata bo fokolang, ho fokotsa ho ntsha mosi.
3. Ha e na halogen ebile ha e na li-ion tsa tšepe e boima.
Kopo:
TF-241 e sebelisoa ho homopolymerization PP-H le copolymerization PP-B. E sebelisoa haholo ho
polyolefin e thibelang malakabe joalo ka hitara ea moea ea mouoane le lisebelisoa tsa ntlo.
Foromo ea Litšupiso bakeng sa 3.2mm PP (UL94 V0):
| Thepa | Foromo S1 | Foromo S2 |
| Homopolymerization PP (H110MA) | 77.3% |
|
| PP ea ho lokisa polima (EP300M) |
| 77.3% |
| Setlolo (EBS) | 0.2% | 0.2% |
| Antioxidant (B215) | 0.3% | 0.3% |
| Thibelo ea ho rotha (FA500H) | 0.2% | 0.2% |
| TF-241 | 22% | 22% |
Thepa ea mechini e ipapisitse le bophahamo ba 30% ba TF-241. Ka 30% TF-241 ho fihlela UL94 V-0(1.5mm)
| Ntho | Foromo S1 | Foromo S2 |
| Sekhahla sa ho cha ka ho otloloha | V0(1.5mm) | UL94 V-0(1.5mm) |
| Lekanyetsa index ea oksijene (%) | 30 | 28 |
| Matla a ho tsikinyeha (MPa) | 28 | 23 |
| Ho lelefatsa nako ea khefu (%) | 53 | 102 |
| Sekhahla sa ho cha ka mor'a ho belisoa ka metsi (70℃, lihora tse 48) | V0(3.2mm) | V0(3.2mm) |
| V0(1.5mm) | V0(1.5mm) | |
| Modulus e flexural (MPa) | 2315 | 1981 |
| Tekanyo ea ho qhibiliha (230℃,2.16KG) | 6.5 | 3.2 |
Ho paka:25kg/mokotla, 22mt/20'fcl ntle le diphalete, 17mt/20'fcl ka diphalete. Ho paka ho hong ho ya ka kopo.
Polokelo:sebakeng se omileng le se pholileng, se bolokehileng hole le mongobo le khanya ea letsatsi, se boloke bophelo ba sona lilemo tse peli.